| POM 507 美國杜邦 |
| 暫無此原料描述部分┄ |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 密度 | --- | ASTM D-792 | 1.42 | --- |
| 物理性能 | 吸水量 | 24hrs浸泡+73�H(+23℃) | ASTM D-570 | 0.25 | % |
| 吸水量 | Equil.50%R.h.+73�H(+23℃) | ASTM D-570 | 0.22 | % | |
| 吸水量 | 浸泡均衡點+73�H(+23℃) | ASTM D-570 | 0.90 | % | |
| 擴散因數 | +73�H(+23℃)106Hz | ASTM D-150 | 0.005 | --- | |
| 機械性能 | 無切口沖擊程度 | +23℃ | ASTM D-256 | 1280 | j/m |
| 壓縮應力 | +73�H@10% Def. | ASTM D-695 | 18.0 | MPsi | |
| 壓縮應力 | +23℃@10% Def. | ASTM D-695 | 124 | MPa | |
| 負載下之變形 | 2000psi@+122�H(14Mpa@50℃) | ASTM D-621 | 0.5 | % | |
| 彎曲疲勞忍耐限度 | +73�H | ASTM D-671 | 4.5 | MPsi | |
| 彎曲疲勞忍耐限度 | +23℃ | ASTM D-671 | 31.0 | MPa | |
| IZOD沖擊強度 | -40�H | ASTM D-256 | 1.2 | ft.lb/in | |
| IZOD沖擊強度 | 40℃ | ASTM D-256 | 64.1 | j/m | |
| IZOD沖擊強度 | +73�H | ASTM D-256 | 1.4 | ft.lb/in | |
| IZOD沖擊強度 | +23℃ | ASTM D-256 | 74.7 | j/m | |
| 拉力沖擊抵抗力 | +73�H | ASTM D-1822 | 100 | ft.lb/in2 | |
| 拉力沖擊抵抗力 | +23℃ | ASTM D-1822 | 200 | kj/m2 | |
| 無切口沖擊程度 | +73�H | ASTM D-256 | 24 | ft.lb/in | |
| 斷裂時之拉力伸張度 | -68�H(-55℃) | ASTM D-638 | 13 | % | |
| 斷裂時之拉力伸張度 | +73�H(+23℃) | ASTM D-638 | 40 | % | |
| 斷裂時之拉力伸張度 | +158�H(+70℃) | ASTM D-638 | 220 | % | |
| 斷裂時之拉力伸張度 | +212�H(+100℃) | ASTM D-638 | >260 | % | |
| 斷裂時之拉力伸張度 | +250�H(+122℃) | ASTM D-638 | >260 | % | |
| 伸張強度 | -68�H | ASTM D-638 | 14.7 | MPsi | |
| 伸張強度 | -55℃ | ASTM D-638 | 101 | MPa | |
| 伸張強度 | +73�H | ASTM D-638 | 10.0 | MPsi | |
| 伸張強度 | +23℃ | ASTM D-638 | 68.9 | MPa | |
| 伸張強度 | +158�H | ASTM D-638 | 6.9 | MPsi | |
| 伸張強度 | +70℃ | ASTM D-638 | 47.5 | MPa | |
| 伸張強度 | +212�H | ASTM D-638 | 5.2 | MPsi | |
| 伸張強度 | +100℃ | ASTM D-638 | 35.9 | MPa | |
| 伸張強度 | +250�H | ASTM D-638 | 3.8 | MPsi | |
| 伸張強度 | +122℃ | ASTM D-638 | 26.2 | MPa | |
| 彈性系數 | +73�H | ASTM D-638 | 450 | MPsi | |
| 彈性系數 | +23℃ | ASTM D-638 | 3100 | MPa | |
| 剪力 | +73�H | ASTM D-732 | 9.5 | MPsi | |
| 剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
| 撓曲系數 | -68�H | 在25℃下 | 570 | MPsi | |
| 撓曲系數 | -55℃ | 在25℃下 | 3930 | MPa | |
| 撓曲系數 | +73�H | 在25℃下 | 410 | MPsi | |
| 撓曲系數 | +23℃ | 在25℃下 | 2830 | MPa | |
| 撓曲系數 | +158�H | 在25℃下 | 230 | MPsi | |
| 撓曲系數 | +70℃ | 在25℃下 | 1585 | MPa | |
| 撓曲系數 | +212�H | 在25℃下 | 135 | MPsi | |
| 撓曲系數 | +100℃ | 在25℃下 | 90 | MPsi | |
| 撓曲系數 | +122℃ | 在25℃下 | 620 | MPa | |
| 彎曲降服強度 | +73�H | ASTM D-790 | 14.1 | MPsi | |
| 彎曲降服強度 | +23℃ | ASTM D-790 | 97.2 | MPa | |
| 壓縮應力 | +73�H@1% Def. | ASTM D-695 | 5.2 | MPsi | |
| 壓縮應力 | +23℃@1%Def. | ASTM D-695 | 35.9 | MPa | |
| 洛氏硬度 | --- | ASTM D-785 | M94,R120 | --- | |
| 摩擦系數 | +73�H(+23℃)靜態(tài) | ThrustWasherTest3 | 0.20 | --- | |
| 摩擦系數 | +73�H(+23℃)動態(tài) | ThrustWasherTest3 | 0.35 | --- | |
| 電氣性能 | 電弧抵抗力 | 120mil(3.1mm) | ASTM D-495 | 220no tracking | Sec. |
| 絕緣強度 | Short Time,90 mils | ASTM D-149 | 500 | V/mil | |
| 絕緣強度 | Short Time,2.3mm | ASTM D-149 | 19.7 | MV/m | |
| 絕緣系數 | +73�H(+23℃)102to106Hz | ASTM D-150 | 3.7 | --- | |
| 電阻系數 | +73�H(+23℃)0.2%H2O | ASTM D-257 | 1015 | ohm-cm | |
| 熱 性 能 | 熱傳導系數 | W/mk | --- | 0.37 | --- |
| 線性熱膨脹系數 | +60 to +104℃ | ASTM D-696 | 13.7 | 10-5m/m.℃ | |
| 線性熱膨脹系數 | +220 to +300�H | ASTM D-696 | 8.3 | 10-5in/in.�H | |
| 線性熱膨脹系數 | +104 to +150℃ | ASTM D-696 | 14.9 | 10-5m/m.℃ | |
| 熱傳導系數 | BTU-in/hr | --- | 2.6 | --- | |
| 熔點 | --- | ASTM D-2133 | 347 | �H | |
| 熔點 | --- | ASTM D-2133 | 175 | ℃ | |
| 線性熱膨脹系數 | -40 to +85�H | ASTM D-696 | 5.8 | 10-5in/in.�H | |
| 線性熱膨脹系數 | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 線性熱膨脹系數 | +85 to +140�H | ASTM D-696 | 6.8 | 10-5in/in.�H | |
| 線性熱膨脹系數 | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 線性熱膨脹系數 | +140 to +220�H | ASTM D-696 | 7.6 | 10-5in/in.�H | |
| 熱變形溫度 | 0.5MPa | ASTM D-648 | 172 | ℃ | |
| 熱變形溫度 | 1.8MPa | ASTM D-648 | 136 | ℃ | |
| 熱變形溫度 | 66psi | ASTM D-648 | 342 | �H | |
| 熱變形溫度 | 264psi | ASTM D-648 | 277 | �H | |
| 可燃燒性 | --- | UL-94 | 94HB | --- | |