D852鈷基堆焊焊條 型號：EDCoCr-E-04
說明：用于耐高溫磨損堆焊焊條,工作溫度1100℃,具有紅硬性,抗烈性.也可用于高溫,高壓閥門熱段模等,同時經(jīng)受沖擊和高溫,耐蝕的部件. HRC≥44
|
Trade- Mark 牌 號 |
Equivalent to China Standard 相當國標 |
Characteristics & application 特性和用途 |
Equivalent to AWS 相當AWS |
| D 802 | EDCoCr-A-03 |
HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter. HRc38-47，耐熱、耐蝕、耐磨。堆焊高溫工件如熱剪切刀刃 |
ECoCr-A |
| D 812 | EDCoCr-B-03 |
HR***5-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve. HR***5-50，耐熱、耐蝕、耐磨。堆焊高溫工件如內燃機閥 |
ECoCr-B |
| D 822 |
HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler. HRc≥53，耐熱、耐磨，但抗沖擊性差。堆焊鍋爐旋轉葉輪 |
||
| D 832 | EDCoCr-C-03 |
HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way. HRc≥50，耐熱、耐磨。堆焊高溫工件如熱軋導軌 |
ECoCr-C |
| D 842 | EDCoCr-D-03 |
HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die. HRc28-38，耐蝕、抗熱疲勞，具有加工硬化性。堆焊熱鍛模 |
|
電焊條 |
硬度 |
化學成分（重量%） |
典型用途 |
|||||||||||
|
C |
Cr |
Si |
W |
Fe |
Mo |
Ni |
Co |
Mn |
|
Cu |
其他 |
|||
|
Sblite 1 |
48 |
2.20 |
29.00 |
2.00 |
14.00 |
3.00 |
0.50 |
3.00 |
Bal |
1.00 |
|
|
|
閥座、軸承、刀口等 |
|
Sblite 6 |
40 |
1.00 |
29.00 |
1.00 |
4.50 |
3.00 |
0.50 |
3.00 |
Bal |
1.00 |
|
|
|
發(fā)動機氣門、高溫高壓閥門、渦輪機葉片 |
|
Sblite 12 |
44 |
1.30 |
29.00 |
1.00 |
9.00 |
3.00 |
0.50 |
3.00 |
Bal |
1.00 |
|
|
|
高溫高壓閥門、鋸齒、螺旋推桿等 |
|
Sblite 21 |
23 |
0.30 |
28.00 |
1.00 |
|
2.50 |
5.50 |
2.50 |
Bal |
2.00 |
|
|
|
渦輪機葉片、閥座、熱沖模 |
|
Sblite 25 |
冷硬 |
0.15 |
20.00 |
1.00 |
14.00 |
3.00 |
0.50 |
10.00 |
Bal |
1.50 |
|
|
|
高溫耐蝕密封面、擠壓模 |
|
Nisble C |
|
0.10 |
17.00 |
|
5.00 |
6.00 |
17.00 |
Bal |
|
|
|
|
|
高溫耐蝕密封環(huán) |
|
Ni-Mang |
冷硬 |
0.60 |
2.70 |
0.20 |
|
Bal |
|
3.70 |
|
13.50 |
|
|
|
錘式破碎機、高錳鋼部件焊接 |
|
STE308-16 |
|
0.08 |
19.50 |
0.90 |
|
Bal |
0.50 |
10.00 |
|
0.80 |
|
0.50 |
|
用于焊接Cr18Ni8不銹鋼 |
|
STE308L-16 |
|
0.03 |
19.50 |
0.90 |
|
Bal |
0.50 |
10.00 |
|
0.80 |
|
0.50 |
|
用于焊接超低碳Cr18Ni8不銹鋼 |
|
STE309-16 |
|
0.15 |
23.50 |
0.90 |
|
Bal |
0.50 |
13.00 |
|
0.80 |
|
0.50 |
|
用于焊接Cr22Nil2不銹鋼及用于不銹鋼與低碳鋼或低合金鋼之間的焊接 |
|
STE309L-16 |
|
0.02 |
23.50 |
0.90 |
|
Bal |
0.50 |
13.00 |
|
0.80 |
|
0.50 |
|
打底層焊接，異種鋼焊接，易產(chǎn)生裂紋部位的焊接 |
|
STE 309Mo-16 |
|
0.12 |
23.50 |
0.90 |
|
Bal |
2.50 |
13.00 |
|
0.80 |
|
|
|
用于焊接Cr22Nil2-Mo不銹鋼 |
|
STE 309MoL-16 |
|
0.03 |
23.50 |
0.90 |
|
Bal |
2.50 |
13.00 |
|
0.80 |
|
|
|
用于焊接超低碳Cr22Nil2Mo不銹鋼 |
|
STE310-16 |
|
0.20 |
26.50 |
0.75 |
|
Bal |
0.50 |
21.50 |
|
1.50 |
|
0.50 |
|
用于焊接Cr25Ni20不銹鋼 |
|
STE 310Mo-16 |
|
0.08 |
26.50 |
0.75 |
|
Bal |
2.50 |
21.00 |
|
1.20 |
|
0.50 |
|
耐硫酸腐蝕、抗裂性、高溫性能優(yōu)良 |
|
STE316-16 |
|
0.05 |
18.50 |
0.90 |
|
Bal |
2.50 |
12.50 |
|
0.80 |
|
0.50 |
|
用于焊接Cr18Ni12Mo2不銹鋼 |
|
STE316L-16 |
|
0.03 |
18.50 |
0.90 |
|
Bal |
2.50 |
12.50 |
|
0.80 |
|
0.50 |
|
用于焊接超低碳Cr18Ni12Mo2不銹鋼 |
|
STE316LF |
|
0.02 |
18.00 |
0.75 |
|
Bal |
2.70 |
16.00 |
|
2.00 |
|
0.50 |
|
耐尿素腐蝕性優(yōu)良 |
|
STE347-16 |
|
0.08 |
19.50 |
0.50 |
|
Bal |
0.50 |
10.00 |
|
0.80 |
|
0.50 |
8xc-1.00 |
用于焊接Cr18Ni8含鈮或鈦的不銹鋼 |
|
STE997 |
56 |
0.60 |
5.50 |
0.80 |
|
Bal |
4.00 |
W:7.0 |
|
0.70 |
|
|
|
低氫型高速鋼焊條 |
|
D 287 |
40 |
0.10 |
14.00 |
0.50 |
|
Bal |
1.00 |
5.00 |
|
0.50 |
|
|
|
水泵、水輪機部件 |
|
D 907 |
冷硬 |
0.20 |
21.00 |
1.00 |
2.50 |
Bal |
3.00 |
|
20.00 |
1.50 |
|
|
|
熱剪刀片 |
|
Delcrome 90sc |
52 |
2.10 |
26.00 |
1.10 |
|
Bal |
|
|
|
0.90 |
|
|
|
挖掘設備、破碎輥、錘 |
|
Delcrome 91 |
55 |
3.00 |
31.00 |
0.60 |
|
Bal |
1.30 |
|
|
0.90 |
|
|
|
破碎機輥、錘頭、泥漿泵部件 |
|
Delcrome 94 |
53 |
3.00 |
31.00 |
0.40 |
|
Bal |
1.30 |
|
|
0.90 |
|
|
|
鏟斗齒、攪拌機、挖掘采礦設備 |
|
Delcrome 945 |
58 |
5.40 |
26.00 |
1.20 |
|
Bal |
|
|
|
1.00 |
|
|
Nb:5.00 |
耐侵蝕、抗高溫腐蝕及磨損場合 |
|
Delcrome 23 |
44 |
0.20 |
5.50 |
1.00 |
|
Bal |
2.50 |
V:7.0 |
|
1.20 |
|
|
|
低氫型焊條，用于鍛模、沖模 |
|
電焊條 |
硬度 |
化學成分（重量%） |
典型用途 |
|
Electrode |
A-91 |
60%碳化鎢、其余為鋼管、A-91中的91為碳化鎢顆粒硬度 |
風機攪拌機葉片、采礦、建筑易損件 |
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||