特征及用途：
焊補(bǔ)鋅、鋁壓鑄模、具良好之耐熱性與耐龜裂性、熱氣沖模、鋁銅熱鍛模、鋁銅壓鑄模、具良好耐熱、耐磨、耐龜裂性。一般熱壓鑄模常有龜甲裂紋狀，大部份是由熱應(yīng)力所引起,亦有因表面氧化或壓鑄原料之腐蝕所引起，熱處理調(diào)至適當(dāng)硬度改善其壽命，硬度太低或太高均不適用。
HRC 40~43
8407-H13焊絲
特 性
|
焊金耐熱 耐腐蝕 耐磨耗性能優(yōu)良,用于修復(fù)基體合金相似的高溫加工工具,如H13鋼.
硬度HRC 43～46度A hot work tool steel that is tungsten free,Good hot hardness up to 565℃.For repair of H-13 tool steels and appications in the die casting and forging industries subject to high thermal gradients.
|
用 途
|
焊補(bǔ)有色金屬壓鑄模具 PA POM PS PE EP Weld-repair non-ferrous bl die-casting molds PA POM PS PE EP
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠
|
特 性
|
Cr W V 多元合金焊絲 ，熔敷金屬具有自硬性的馬氏體組織。具有高硬度耐高溫沖擊，焊后機(jī)加工困難。硬度HRC48～52 Cr multielement alloy welding wire, w. v. deposited bl has since the rigid martensite organization. With high hardness, impact resistant machining difficulty after welding. Hardness HRC48 ~52
|
用 途
|
焊補(bǔ)熱鍛模 沖模 熱加工工具 熱切模等Hot forging die weld-repair hot-working tools etc. Eagerly
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
焊金耐疲勞 耐熱 耐磨耗沖擊,一般熱壓鑄模具常有龜裂紋狀,大部分是熱應(yīng)力引起,熱處理調(diào)至適當(dāng)硬度改善其壽命,硬度太高或太低均不適用.HRC43～47 Welding gold fatigue resistance, abrasion resistance impact resistant heat die-casting molds, most often turtle crack is caused by thermal stress, heat treatment to improve its service life, suitable hardness hardness too much or too little are not applicable.
|
用 途
|
焊補(bǔ)熱氣沖模,銅鋁鋅熱鍛模,鋁擠壓模. Hot stamping, weld-repair copper aluminum and zinc hot forging, aluminum extrusion die
.
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
放電加工,焊接性好,研磨后光滑如鏡,加入易切削元素,切削加工容易,溶敷金屬具有高韌性,耐磨不變形等特點(diǎn),焊后只要簡單熱處理即可得到均一的鏡面效果. 750an electro-discharge machining, welding, grinding smooth as a mirror, after joining cutting elements, machining, easy dissolve deposited bl with high toughness and wear no debation characteristics, such as simple after welding heat can get the mirror effect unib.
|
用 途
|
焊補(bǔ)塑膠模具NAK55 NAK80等NAK55 NAK80 weld-repair plastic mould etc
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
馬氏體時效鋼,其堆焊層硬度可達(dá)HRC30～32度,溶敷金屬柔軟,具韌性易切削,在其500℃/2H時效處理后硬度可提高到HRC48～50度. Limitation of martensite steel, the hardfacing layer of hardness HRC30 ~ 32 degrees, soluble bl soft, apply, in its toughness cutting 500 ° c / 2H aging treatment can improve HRC48 hardness to 50 ~.
|
用 途
|
焊補(bǔ)鋁壓鑄模具,擠壓模具,沖裁模 注塑模等. Weld repairs, aluminum casting die, extrusion dies, punching mould injection mold, etc
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
含有W Mo Cr V 的高合金焊絲,溶敷金屬具有高韌性,高硬度沖擊耐磨耗性能,可使用在600℃的熱間環(huán)境,焊后金屬可高達(dá)HRC61～63度,經(jīng)熱處理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited bl with high toughness and high hardness, impact abrasion resistance perbance can be used in 600 degrees Celsius between thermal environment, after welding bl can be as high as HRC61 ~ 63 degree of hardness, still improve.
|
用 途
|
焊補(bǔ)冷熱作模具,成型刀具,修整刀具 沖頭 模具 粉碎機(jī)刃口,沖壓模具,也可以在碳鋼和低合金鋼上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made on new tools. #
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
可直接在各種鑄鐵/生鐵材料模具上施焊,也可以做為模具龜裂之焊合,用短弧焊接較不易產(chǎn)生氣孔及裂痕. But in all sorts of cast iron/directly on the mould material, also can make the mold cracked, with a short weld arc soldering less porosity and crack.
|
用 途
|
焊補(bǔ)鑄鐵,易加工雕刻. Iron, easy machining weld-repair carving.
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
特 性
|
熔敷金屬能滿足較高的焊接質(zhì)量和耐腐蝕性能. Deposited bl can meet high welding quality and corrosion resistance.
|
用 途
|
用于鑄鐵 碳鋼 不銹鋼和低合金鋼的焊接. For carbon steel and low alloy steel iron welding.
|
規(guī) 格
|
1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠ 3.2￠
|
特 性
|
含鎳鉻成份高,拉力強(qiáng) 硬度HB-300. Containing nickel chrome component high hardness, tensile strong HB - 300
.
|
用 途
|
異材焊接 硬面制作打底,高強(qiáng)度鋼接合 龜裂焊補(bǔ). Different welding materials production, hardfaced with high strength steel render junction weld-repair cracked
|
規(guī) 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
氬弧焊銅 優(yōu)異的機(jī)械加工性能 硬度HB-200. Argon arc welding copper excellent machining perbance hardness HB - 200.
|
用 途
|
廣泛用于電解片 銅合金 鋼 青銅 生鐵銅件之焊補(bǔ). Widely used in electrolytic copper alloy steel cast bronze pieces of copper pieces of weld-repair.
|
規(guī) 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
馬氏體不銹鋼,耐腐蝕,拋光性能優(yōu)異,熱處理性能穩(wěn)定 硬度HRC51~53. Martensitic stainless steel corrosion resistance, excellent polishing treatment stable perbance HRC51 hardness - 53.
|
用 途
|
適用于420不銹鋼的焊接. Applicable to 420 stainless steel welding.
|
規(guī) 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|
特 性
|
以焊接開裂敏感性低的合金成份設(shè)計,含鎳約1%機(jī)械加工性能與蝕刻性優(yōu)越,焊后硬度
HRC30~34. n cracking sensitivity low alloy welding components design, containing nickel about 1% of machining perbance and etching of superior, postweld hardness
HRC30 ~ 34.
|
用 途
|
塑膠模具的焊補(bǔ). Plastic mould weld-repair.
|
規(guī) 格
|
0.9￠ 1.2￠ 1.6￠ 2.0￠
|