| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.91 | g/cm3 | ||
| 熔體流動速率 | 230℃，2.16kg | ASTM D-1238 | 25 | g/10min | ||
| 機(jī)械性能 | IZOD沖擊強(qiáng)度 | 1/4"，23℃ | ASTM D-256 | 8 | kg.cm/cm | |
| 彎曲模量 | ASTM D-790 | 13500 | KG/cm2 | |||
| 斷裂伸長率 | 50mm/min | ASTM D-638 | ＞150 | % | ||
| IZOD沖擊強(qiáng)度 | 1/4"，0℃ | ASTM D-256 | 5 | kg.cm/cm | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 85 | R Scale | ||
| IZOD沖擊強(qiáng)度 | 1/4"，-20℃ | ASTM D-256 | 4 | kg.cm/cm | ||
| 抗張強(qiáng)度 | 屈服 | 50mm/min | ASTM D-638 | 290 | KG/cm2 | |
| 斷裂 | 50mm/min | ASTM D-638 | 200 | KG/cm2 | ||
| 熱性能 | 維卡軟化點 | 1kg | ASTM D-1525 | 152 | ℃ | |
| 可燃性 | 1/8" | UL 94 | HB | |||
| 可燃性 | 1/16" | UL 94 | HB | |||
| 熱變形溫度 | 4.6kg/cm2(1/8") | ASTM D-648 | 110 | ℃ | ||
| 熔點 | DSC | SGC | 160 | ℃ | ||