| 性能項(xiàng)目 | 測(cè)試條件 | 測(cè)試方法 | 數(shù)值/描述 | 單位 | |
| 機(jī)械性能 | 拉伸強(qiáng)度(引張強(qiáng)度) | ASTM D638/ISO 527 | 260 | kg/cm²(MPa)[Lb/in2] | |
| 斷裂伸長(zhǎng)率 | ASTM D638/ISO 527 | >200 | % | ||
| 拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
| 拉伸屈服伸長(zhǎng)率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸斷裂伸長(zhǎng)率(延伸率) | ASTM D638/ISO 527 | % | |||
| 彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 11500 | kg/cm²(MPa)[Lb/in2] | ||
| 彎曲強(qiáng)度 | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in2] | |||
| 洛氏硬度 | ASTM D785 | 85 | kg·cm/cm(J/M)ft·lb/in | ||
| IZOD 缺口沖擊強(qiáng)度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | N.B | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy沖擊強(qiáng)度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（無(wú)缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（無(wú)缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 0.9 | ||
| 成型收縮率 | ASTM D955 | 1.4~1.8 | % | ||
| 熔融指數(shù)（流動(dòng)系數(shù)） | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
| 熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | ℃（℉） | |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 維卡軟化點(diǎn) | ASTM D1525/ISO R306 | ℃（℉） | |||
| 熔點(diǎn) | - | ℃（℉） | |||
| 燃燒性（率） | UL94 | 1/16"HB | |||
| 線(xiàn)性膨脹系數(shù) | ASTM D696/ISO 11359 | mm/mm.℃ | |||
| 加工條件 | 干燥條件 | ||||
| 加工溫度 | 射嘴 | ℃ | |||
| 料筒前段 | ℃ | ||||
| 料筒中段 | ℃ | ||||
| 料筒后段 | ℃ | ||||
| 熔體溫度 | ℃ | ||||
| 模具溫度 | ℃ | ||||
| 壓力 | 注塑壓力 | Mpa | |||
| 保壓壓力 | Mpa | ||||
| 背壓 | Mpa | ||||
| 螺桿轉(zhuǎn)速 | rpm | ||||
| 其他 | 備注 | 高耐沖擊 | |||
| 顏色 | 奶白 | ||||
| 特性 | 油漆桶 | ||||
| 用途 | |||||