| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | ASTM D-1238 | 2.5 | g/10min. | |
| 機(jī)械性能 | Izod沖擊強(qiáng)度 | ASTM D-256 | 2.2(22) | kg-cm/cm(J/m) | |
| 抗張強(qiáng)度 | ASTM D-638 | 520(51) | kg/cm2(MPa) | ||
| 彎曲模數(shù) | ASTM D-790 | 3.4(3330) | kg/cm20000(MPa) | ||
| 伸長(zhǎng)率 | ASTM D-638 | 2.3 | % | ||
| 抗張模數(shù) | ASTM D-638 | 1.8(1770) | kg/cm20000(MPa) | ||
| 彎曲強(qiáng)度 | ASTM D-790 | 1000(98) | kg/cm2(MPa) | ||
| 熱性能 | 衛(wèi)氏軟化點(diǎn) | ASTM D-648 | 102 | ℃ | |
| 衛(wèi)氏軟化點(diǎn) | ASTM D-1525 | 102 | ℃ | ||
| 熱變形溫度 | ASTM D-648 | 95 | ℃ | ||
| 熱變形溫度 | ASTM D-1525 | 95 | ℃ | ||
| 其它性能 | 殘留單體 | 700 | ppm max | ||