| 規(guī)格級別 | 注塑 其它 耐磨, 增強 | 外觀顏色 | |
| 該料用途 | 齒輪、襯套、凸輪和其它耐磨擦的應(yīng)用。 | ||
| 備注說明 | 加工特性：一般等級,添加20% TEFLON3纖維，表面潤滑。產(chǎn)品特性：與500相似的物理性能，但有超低的磨擦系數(shù)與高度耐磨耗率。 | ||
| 加工條件 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.72 | % |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.20 | % | |
| 吸水量 | 50%相對濕度 | ASTM D-570 | 0.18 | % | |
| 物理性能 | 模收縮 | 3.2mm | 1.9-2.2 | % | |
| 比重 | ASTM D-792 | 1.54 | |||
| 機械性能 | 破裂點拉伸變形量 | 100℃ | ASTM D-638 | 160 | % |
| 拉伸強度 | 70℃ | ASTM D-638 | 32 | MPa | |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 10 | % | |
| 撓曲疲勞忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 24 | MPa | |
| 拉伸強度 | -55℃ | ASTM D-638 | 74 | MPa | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 830 | MPa | |
| 壓縮應(yīng)力 | 23℃,10%變形 | ASTM D-695 | 90 | MPa | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 2890 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 48 | MPa | |
| 拉伸強度 | 122℃ | ASTM D-638 | 19 | MPa | |
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 3730 | MPa | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 585 | MPa | |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | 40 | % | |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 72 | MPa | |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | 190 | % | |
| 負(fù)載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.6 | % | |
| IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 32 | j/m | |
| 拉伸強度 | 100℃ | ASTM D-638 | 23 | MPa | |
| 洛氏硬度 | ASTM D-785 | 78 | M scale | ||
| IZOD沖擊試驗 | 23℃ | ASTM D-256 | 37 | j/m | |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 2410 | MPa | |
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1380 | MPa | |
| 壓縮應(yīng)力 | 23℃,1%變形 | ASTM D-695 | 31 | MPa | |
| 洛氏硬度 | ASTM D-785 | 118 | R scale | ||
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 15 | % | |
| 抗剪強度 | 23℃ | ASTM D-732 | 55 | MPa | |
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 66 | kj/m2 | |
| 電氣性能 | 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 15.8 | kv/mm |
| 介電因數(shù) | 50%RH,23℃,106Hz | ASTM D-150 | 0.009 | ||
| 容積電阻率 | 23℃,0.2%含水量 | ASTM D-257 | 3×1016 | Ω.cm | |
| 抗電弧 | 3.1mm | ASTM D-495 | 183 | sec | |
| 介電常數(shù) | 50%RH,23℃,102～106Hz | ASTM D-150 | 3.1 | Ω.cm | |
| 熱性能 | 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 10.4 | 10-5m/m℃ |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 118 | ℃ | |
| 熔點 | ASTM D-2133 | 175 | ℃ | ||
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 168 | ℃ | |
| 自燃性 | UL 94 | HB | |||
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 12.2 | 10-5m/m℃ | |