| 性能項目 | 測試條件 | 測試方法 | 數(shù)值/描述 | 單位 | |
| 機械性能 | 拉伸強度(引張強度) |
|
ASTM D638/ISO 527 | 67 | kg/cm2(MPa)[Lb/in2] |
| 斷裂伸長率 |
|
ASTM D638/ISO 527 |
|
% | |
| 拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] | |
| 拉伸屈服伸長率(延伸率) |
|
ASTM D638/ISO 527 | 85 | % | |
| 拉伸斷裂伸長率(延伸率) |
|
ASTM D638/ISO 527 |
|
% | |
| 彎曲模量(彎曲彈性率) |
|
ASTM D790/ISO 178 | 2740 | kg/cm2(MPa)[Lb/in2] | |
| 彎曲強度 |
|
ASTM D790/ISO 178 | 96 | kg/cm2(MPa)[Lb/in2] | |
| 洛氏硬度 |
|
ASTM D785 | 94 |
|
|
| IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" 23℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| Charpy沖擊強度 | 23℃ （缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | |
| -30℃（缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（無缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（無缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 物性性能 | 比重（密度） |
|
ASTM D792/ISO 1183 | 1.42 |
|
| 成型收縮率 |
|
ASTM D955 |
|
% | |
| 熔融指數(shù)（流動系數(shù)） | 200℃/5kg | ASTM D1238/ISO 1133 |
|
g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 |
|
g/10min | ||
| 吸水率 23℃/24H |
|
ASTM D570/ISO 62 | 0.2 | % | |
| 熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | 130 | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 |
|
℃（℉） | ||
| 維卡軟化點 |
|
ASTM D1525/ISO R306 |
|
℃（℉） | |
| 熔點 |
|
- |
|
℃（℉） | |
| 燃燒性（率） |
|
UL94 | HB |
|
|
| 線性膨脹系數(shù) |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ | |
| 電氣性能 | 介電常數(shù) | 100HZ | ASTM D150/IEC 60250 |
|
|
| 1MHZ | ASTM D150/IEC 60250 |
|
|
||
| 體積電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω.cm | |
| 表面電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω | |
| 耐電弧性 |
|
ASTM D495/IEC 60112 |
|
|
|
| 加工條件 | 干燥條件 |
|
|
|
|
| 加工溫度 | 射嘴 |
|
|
℃ | |
| 料筒前段 |
|
|
℃ | ||
| 料筒中段 |
|
|
℃ | ||
| 料筒后段 |
|
|
℃ | ||
| 熔體溫度 |
|
|
|
℃ | |
| 模具溫度 |
|
|
|
℃ | |
| 壓力 | 注塑壓力 |
|
|
Mpa | |
| 保壓壓力 |
|
|
Mpa | ||
| 背壓 |
|
|
Mpa | ||
| 螺桿轉(zhuǎn)速 |
|
|
|
rpm | |
| 其他 | 備注 |
|
|||
| 顏色 |
|
||||
| 特性 | 高粘度 | ||||
| 用途 |
|
||||