| 分類: | E8016-G, SFA/AWS A5.5, E 50 6 Mn1Ni B 12 H5, EN ISO 2560-A |
| 認(rèn)證: | E8016-G, ABS, EN 13479, CE, 10.105.16, DB, 3Y H5, DNV, 6Y H5, GL, 5Y42 H5, LR, 2.5-4.0 mm, NAKS/HAKC, 4Y H5, RS, 06107, VdTüV, UNA 272581, Seproz |
Approvals are based on factory b. Please contact ESAB for more inbation.
| Alloy Type: | C, Mn, 1% Ni |
| Coating Type: | Basic |
| Diffusible Hydrogen: | <5.0 ml/100g |
| Welding Current: | AC, DC+(-) |
| Impact Value | Testing Temperature |
| ISO As welded | |
| 115 J | -40 °C |
| 100 J | -60 °C |
| Elongation | Tensile Strength | Yield Strength |
| ISO As welded | ||
| 27 % | 640 MPa | 560 MPa |
| AWS As welded | ||
| - | - | - |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 59 hr | 0.65 kg | 87 | 55-85 A | 0.7 kg/h | 24 V | 2.5 x 350 mm |
| 69 hr | 0.59 kg | 54.5 | 80-140 A | 0.96 kg/h | 21.4 V | 3.2 x 350 mm |
| 106 hr | 0.62 kg | 26.8 | 110-170 A | 1.27 kg/h | 21.5 V | 4.0 x 450 mm |
| 109 hr | 0.63 kg | 16.9 | 180-230 A | 1.95 kg/h | 22.6 V |
5.0 x 450 mm |