EXTEM VH1003P Resin SABIC Innovative Plastics Asia Pacific PEI，EXTEM? VH1003P resin
聚醚酰亞胺
SABIC Innovative Plastics Europe
產(chǎn)品說(shuō)明：
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Powder version of VH1003. This resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited. RoHS compliant.
外觀：清晰/透明
形式：粉狀
加工方法：注射成型
EXTEM? VH1003P resin 物性表
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
比重 |
1.30 |
g/cm3 |
ASTM D792, ISO 1183 |
|
熔流率（熔體流動(dòng)速率）(367°C/6.6 kg) |
16 |
g/10 min |
ASTM D1238 |
|
溶化體積流率（MVR）(360°C/5.0 kg) |
8.50 |
cm3/10min |
ISO 1133 |
|
收縮率 |
|
|
內(nèi)部方法 |
|
流動(dòng) 1 |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
流動(dòng) : 3.20 mm |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
橫向流動(dòng) : 3.20 mm |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
吸水率 |
|
|
ISO 62 |
|
飽和, 23°C |
1.8 |
% |
ISO 62 |
|
平衡, 23°C, 50% RH |
0.60 |
% |
ISO 62 |
|
注射 |
額定值 |
單位制 |
|
|
干燥溫度 |
149 |
°C |
|
|
干燥時(shí)間 |
4.0 到 6.0 |
hr |
|
|
干燥時(shí)間，最大 |
24 |
hr |
|
|
建議的最大水分含量 |
0.020 |
% |
|
|
建議注射量 |
40 到 60 |
% |
|
|
料筒后部溫度 |
360 到 382 |
°C |
|
|
料筒中部溫度 |
371 到 393 |
°C |
|
|
料筒前部溫度 |
382 到 404 |
°C |
|
|
射嘴溫度 |
377 到 399 |
°C |
|
|
加工（熔體）溫度 |
382 到 404 |
°C |
|
|
模具溫度 |
135 到 163 |
°C |
|
|
背壓 |
0.345 到 0.689 |
MPa |
|
|
螺桿轉(zhuǎn)速 |
40 到 70 |
rpm |
|
|
排氣孔深度 |
0.025 到 0.076 |
mm |