PC/ABS合金料南沙GE C6200無(wú)鹵阻燃V0 耐沖擊
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 模具收縮率 | 3.2mm | ASTM D-955 | - | E-3 |
| 比重 |
|
ASTM D-792 | - |
|
|
| 吸水率 |
|
ASTM D-570 | - | % | |
| 機(jī)械性能 | 沖擊強(qiáng)度缺口 | 23℃ | ASTM D-256 | 535 | J/m |
| 拉伸強(qiáng)度(屈伏點(diǎn)) |
|
ASTM D-638 | 67 | Mpa | |
| 彎曲模量 |
|
ASTM D-790 | 2691 | Mpa | |
| 彎曲強(qiáng)度 |
|
ASTM D-790 | 103 | Mpa | |
| 拉伸率(斷裂點(diǎn)) |
|
ASTM D-638 | 50 | % | |
| 拉伸模量 |
|
ASTM D-638 | - | Mpa | |
| 洛氏硬度 |
|
ASTM D-785 | - | R | |
| 電氣性能 | 表面電阻 |
|
ASTM D-257 | - | Ohm-cm |
| 損耗因數(shù) | 1MHz | ASTM D-150 | - |
|
|
| 體積電阻 |
|
ASTM D-257 | - | Ohm-cm | |
| 介電常數(shù) | 1MHz | ASTM D-150 | - |
|
|
| 熱性能 | 阻燃性 |
|
UL-94 | 1.5 | UL94 |
| 熱變形溫度 | 1.8Mpa | ASTM D-648 | 86 | ℃ | |
| UL長(zhǎng)期使用溫度 | 無(wú)沖擊 | UL-746B | 75 | ℃ | |
| 維卡軟化點(diǎn) |
|
ASTM D-525 | - | ℃ | |
| 熱變形溫度 | 0.45Mpa | ASTM D-648 | - | ℃ | |
| 阻燃性 |
|
UL-94 | V-0 |
|
|
| 線(xiàn)膨脹系數(shù) |
|
E831 | - | 1/℃ | |
| UL長(zhǎng)期使用溫度 | 含沖擊 | UL-746B | 65 | ℃ | |
PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和丙烯腈-丁二烯-苯乙烯共聚物（ABS）合并而成的熱可塑性塑膠，結(jié)合了兩種材料的特性，ABS材料的成型性和PC的機(jī)械性、沖擊強(qiáng)度和耐溫、抗紫外線(xiàn)（UV）等性質(zhì)，顏色是無(wú)色透明顆粒，可使用在汽車(chē)內(nèi)部零件、商務(wù)機(jī)器、通信器材、家電用品及照明設(shè)備上。
干燥處理：加工前的干燥處理是必須的。濕度應(yīng)小于0.04%，建議干燥條件為90~110C，2~4小時(shí)。
注射速度：盡可能地高。
化學(xué)和物理特性: PC/ABS具有PC和ABS兩者的綜合特性。例如ABS的易加工特性和PC的優(yōu)良機(jī)械特性和熱穩(wěn)定性。二者的比率將影響PC/ABS材料的熱穩(wěn)定性。PC/ABS這種混合材料還顯示了的流動(dòng)特性。收縮率在0.5%左右。