C
|
Si
|
Mn
|
P
|
S
|
Cr
|
其它元素
|
～0.25
|
～0.30
|
～0.40
|
≤0.025
|
≤0.003
|
～14.0
|
添加
|
熱膨脹系數(shù)
【10-6m/(m x K)】 |
20-100°C
|
20-200°C
|
20-300°C
|
20-400°C
|
20-500°C
|
10.5
|
11.0
|
11.0
|
|||
熱傳導性
【W(wǎng)／(m X K)】; |
20°C
|
350°C
|
700°C
|
||
24.0
|
25.0
|
26.0
|
膨脹系數(shù)
【10-6m/(m x K)】 |
20-100°C
|
20-200°C
|
20-300°C
|
20-400°C
|
20-500°C
|
10.5
|
11.0
|
11.0
|
|||
段造
|
軟性退火
|
淬 硬
|
回 火
|
||
1050-850°C
|
730-780°C
|
1000-1030°C
|
250-600°C
|
||
出廠狀態(tài)
|
運用狀態(tài)
|
鋼材組織
|
退火，最大硬度至250HBW
|
50-55 HRC
|