材質(zhì)
|
用途
|
化學(xué)成分
|
力學(xué)能力
|
線徑（mm）
|
凈重(kg)
|
閥芯直徑(mm)
|
備注
|
ER304
|
主要用于焊接18Cr-8Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.08-0.45
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER304L
|
主要用于焊接17Cr-8Ni鋼
|
C:0.028%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER308
|
主要用于焊接19Cr-9Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER308L
|
主要用于焊接20Cr-9Ni鋼
|
C:0.024%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:20.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.8-4.5
|
5/12.5/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER309
|
主要用于焊接20Cr-13Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER309L
|
主要用于焊接20Cr-14Ni鋼
|
C:0.024%
Mn:1.65%
Si:0.42%
Ni:14.33%
Cr:20.10%
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER309Lsi
|
主要用于焊接20Cr-14Ni鋼
|
C:0.024%
Mn:1.65%
Si:1.02%
Ni:14.33%
Cr:20.10%
|
拉伸強(qiáng)度Mpa1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER321
|
主要用于焊接16Cr-7Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:8.33%
Cr:17.10%Ti0.73
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER347
|
主要用于焊接16Cr-9Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300 0
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER347L
|
主要用于焊接17Cr-9Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:9.33%
Cr:17.10%
（Ta+Nb）（10*C）-10
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300 0
|
MIG:0.8-1.6
TIG:1.0-4.5
|
ER316
|
主要用于焊接16Cr-9Ni鋼
|
C:0.064%
Mn:1.65%
Si:0.42%
Ni:10.33%
Cr:17.10%
Mo2.03
|
拉伸強(qiáng)度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6
TIG:1.0-4.5
|